塑料摩擦系数测试仪  状态调节

状态调节按GB2918-82《塑料试样状态调节和试验的标准环境》进行，温度为23?5摄氏度，温度为50?10%。

塑料摩擦系数测试仪  结果计算

1、单个试样的结果计算

1.1本标准以磨痕度来表征磨损量。测量三点，取平均值，各点之差不得大于1毫米。在需要时，也可用体积磨损表示磨损量。

体积磨损V（厘米的3次方）可用式（1）计量：

特点：

1、系统运行稳定，可靠性高。

2、结构紧凑，使用方便，简单。

3、采用高精度电机、驱动机、传感器，精度高。

4、具有试验人员分级管理功能。

5、实时显示摩擦系数-时间，扭矩-时间曲线。

6、试验报告可打印试验参数，试验数据，曲线，备注等信息，简单，方便，可编辑。

Characteristic:

1. The system runs steadily and has high reliability.

2. The structure is compact, easy to use and simple.

3, using high precision motor, drive and sensor, high accuracy.

4. It has the function of grading management of the testers.

5, real-time display of friction coefficient time, torque time curve.

6. The test report can print experimental parameters, test data, curves, remarks and other information. It is simple, convenient and editable.

精度Precision:

1、速度精度：1%  Speed precision: 1%

2、负荷精度：0.5%   Load precision: 0.5%

3、摩擦力矩精度：1%   The precision of friction moment: 1%

4、计数器精度：1S。  Counter precision: 1S

5、传感器测量精度：1% FS  Sensor measurement accuracy: 1% FS

橡胶摩擦磨耗的影响因素

橡胶的磨耗主要有三种形式：

1.磨损磨耗：粗糙表面上凸出的尖锐粗糙物不断切割，刮擦

2.疲劳磨耗：硫化胶表面受周期性压缩，剪切，拉伸等形变作用

3.卷曲磨耗：光滑表面接触时硫化胶表面的微凹凸不平的地方发生变形。

影响因素：

实际接触面积的影响：

1.粘附阻力的大小与两表面的微观接触面积的总和成比例

2.在一定温度下，随着负荷的增加而产生的橡胶变形使橡胶与摩擦表面的粘结密度增加，从而使摩擦力增加

特点：

1、速度精度：1%

2、负荷精度：0.5%

3、摩擦力矩精度：1%

4、具有试验人员分级管理功能。

5、实时显示摩擦系数-时间，扭矩-时间曲线。

6、试验报告可打印试验参数，试验数据，曲线，备注等信息，简单，方便，可编辑。

7、试样尺寸：30mm?7mm?6mm

8、转动速度：0-500转/分 （可调）

9、负 荷：196N ? 0.1%（可增至392N）

10、摩擦环尺寸：￠40?10mm，倒角0.5?45?，外圆表面与内圆同心度偏差小于0.01

11、摩擦环材质：45号钢,淬火,热处理HRC40-45,外圆表面光洁度▼8

12、摩擦力矩：0--4N?m

13、砝码重量：4KG砝码一件，1KG砝码4件，可实现重量叠加功能。

14、计数器精度：1S

15、传感器测量精度：1% FS

16、系统运行稳定，可靠性高。

17、结构紧凑，使用方便，简单。

18、采用高精度电机、驱动机、传感器，精度高。

19、主要配置及附件：（计算机控制）

1、试验主机一台

2、高精度扭矩传感器一只

3、计算机数据采集卡一块

4、计算机一台（品牌）

5、彩色激光喷墨打印机一台

6、计算机控制软件一套

7、4Kg砝码两件（备用一套）

8、标准磨擦环四件（备用两件）

9、产品使用说明书一份

10、产品合格证

11、产品装箱单一份

12、整机重量：约87公斤

适用范围：

适用于塑料制品、橡胶制品、石墨板材或其他复合材料的滑动摩擦，磨损性能测试，也可对试验中试样的磨擦力、磨擦系数和磨损量进行测定。也可对试验中试样的磨擦力、磨擦系数和磨损量进行测定。

Scope of application:

It is suitable for sliding friction, wear testing of plastic products, rubber products, graphite plate or other composite materials. It can also be used to measure the friction force, friction coefficient and wear amount of the test sample. The friction force, friction coefficient and wear volume of the specimens can also be measured.

技术参数Technical parameters：  M-200

1、试样尺寸：30mm?7mm?6mm；sample size: 30mm x 7mm x 6mm;

2、转动速度：≤200转/分（可调）；rotation speed: less than 200 turn / points (adjustable);

3、负荷：(20KG)196N ? 0.1%,可增至(40KG)392N；load: (20KG) 196N 0.1%, which can be increased to (40KG) 392N;

4、摩擦环尺寸：≥￠40?10mm，倒角≥0.5?45?，外圆表面与内圆同心度偏差≤0.01；the size of the friction ring is greater than or equal to 40 x 10mm, the chamfering is equal to 0.5 x 45 degrees, and the concentricity deviation between the outer surface and the inner circle is less than 0.01.

5、摩擦环材质：45号钢；friction ring material: No. 45 steel;

6、摩擦力矩：0—4N.m；friction torque: 0 - 4N.m;

7、砝码重量：4KG砝码十件，1KG砝码十件，可实现重量叠加功能；weight weight: 4KG weight ten, 1KG weight ten, can achieve weight superposition function.

8、精度：速度精度≤1%；负荷精度≤0.5%；摩擦力矩精度≤1%；计数器精度≤1S；传感器测量精度≤1%F。accuracy: speed accuracy is less than 1%; load accuracy is less than 0.5%; friction torque accuracy is less than 1%; counter accuracy is less than 1S; sensor measurement accuracy is less than 1%F.

试验报告

试验报告应包括下列内容：

A.塑料名称、规格、牌号、生产厂；

B.试样的制备方法，摩擦表面状况，测定的试样个数；

C.环境温度、温度及状态调节条件；

D.圆环材质、硬度、光洁度和外径尺寸；

E.试验负荷；

F.试验结果：磨痕宽度或体积磨损及摩擦系数的测定结果；

G.试验日期、人员。

试验设备

1、传动系统，用来带动圆环以给定的转速旋转，精确到5%以内，并要求圆环安装部位轴的径向跳动小于0.01毫米。

2、加载系统，对试样和圆环，可施加法向力，精确到5%以内。

3、测定和记录摩擦力矩系统，精确到5%以内。

4、记录圆环转数的计数器或记时器，精确到1%以内。

5、试样夹具结构和尺寸见图2，并附配垫圈4 GB 848-76，沉头螺钉M3?0.35长10毫米。要保证试样安置后无轴向窜动。

注：试验设备本标准推荐采用M-200型磨损试验机。

6、本试验中圆环的材质对塑料磨损试验结果影响很大，因此本标准采用的圆环，其外形尺寸见图3。

材料为45号钢，圆环要求整体淬火，热处理HRC 40～45，外圆表面光洁度▽8，倒角处均为0.5?45度，外圆表面与内圆同心度偏差小于0.01.

    圆环可以反复使用，每次试验后，需重新磨削。当外径小于36毫米就不能再用。作仲裁试验时必须用直径40毫米的圆环。

注：圆环材质也可按产品标准另定。

投诉体系及联系方式

1、 如果您对我们的服务有意见，请向技术部调度员或维修部经理投诉。

2、 对用户所投诉的问题，核实是我们责任的，将对管理人员及经办人员进行不同程度的惩处。如不是我司的责任，相关人员也将向用户说明情况并帮助客户解决问题。

服务

1．供方质量保证体系严格按照ISO9001质量标准之要求执行

2．培训：可根据客户要求在设备出厂前或设备到场后，对需方的技术人员进行操作、保养及设备维护进行技术培训

3．服务：当设备因质量或其他原因不能正常工作时，我公司在得到通知后24小时内给予答复；需要现场维修时，我公司在得到通知后48小时内派员上门维修、检测

4．设备保修期为1年。